PENINGKATAN NILAI KUAT TEKAN DAN PERBAIKAN RETAK-RETAK PADA BETON DENGAN MENGGUNAKAN FIBER KAWAT BENDRAT BENTUK “Z” DENGAN 3 (TIGA) VARIASI CAMPURAN

Indonesia

Authors

  • Juanita Juanita

DOI:

https://doi.org/10.31949/jensitec.v8i01.1982

Keywords:

Bendrat, Compressive Strength, Crack

Abstract

Concrete is the main basic material used for the planning and design of widely used structures. This is because concrete has a very high compressive strength value when compared to other materials. However, concrete also has weaknesses, one of which is its brittle nature. Therefore, in this study, the use of Z-shaped bendrat wire will be carried out to increase the value of the compressive strength of concrete while improving the brittle nature of the concrete.In this study, bendrat wire fiber in the form of Z was used with a mixed variation of 0.5%, 0.75% and 1%. The number of test objects made is 12 pieces. The test was carried out when the specimen was 28 days old by using a Compression Testing Machine (CTM). From the results of the study, the average compressive strength value for normal concrete (SN) was 26.46 MPa, for Z-shaped bendrat wire fiber concrete with a mixed variation of 0.5% (SF1) the average compressive strength value was 27.27 MPa, for fiber concrete bendrat wire Z shape with a mixed variation of 0.75% (SF2) the average compressive strength value is 28.03 MPa, and for fiber concrete wire bendrat Z shape with a mixed variation of 1% (SF3) the average compressive strength value is 28.21 MPa. The more Z-shaped bendrat wire fibers added to the concrete mix, the higher the compressive strength value and the smaller the cracks that occur in the concrete.

Downloads

Download data is not yet available.

References

[1] Tjokrodimuljo, Kardiyono. Teknologi Beton, Nafiri, Yogyakarta.1996.
[2] Tambunan, R., dan Priyono, B.S. Peningkatan Kualitas Beton dengan Penambahan Viber Bendrat, Jurnal Rancang Sipil 1(1), Desember 2012, Jurusan Teknik Sipil,
Fakultas Teknik Sipil dan Perencanaan Institut Teknologi Medan.2012.
[3] Ariatama, Ananta. Pengaruh Pemakaian Serat Kawat Berkait pada Kekuatan Beton Mutu Tinggi Berdasarkan Optimasi Diameter Serat, Tesis, Program Pascasarjana Universitas Diponogoro Semarang.2007.
[4] Sahay, N.S., dan Ngini, G. Pengaruh Penambahan Kawat Bendrat pada Campuran Beton terhadap Kuat Tekan Beton, 5(2), Desember 2010 ISSN 1412-3388, Universitas Palangka Raya
[5] Irvan, RKP., 2017 “Pengaruh Penambahan Serat Kawat Bendrat Berbentuk “U” Terhadap Sifat Mekanis Beton”., Jom FTEKNIK. Volume 4 No.2.
[6] Uluhiyah, Abdalia., 2018 “Pengaruh Penambahan Serat Bendrat dan Penambahan Serbuk Kaca Sebagai Pengganti Sebagian Agregat Halus Terhadap Sifat Mekanika Beton” Universitas Mataram : Mataram.
[7] Suhendro., 2000 “Beton Fiber Konsep, Aplikasi dan Permasalahannya”., Universitas Gajah Mada : Yogyakarta.
[8] Anonim, 2000, SNI 03-2834-2000”Metode Penelitian Campuran Beton Normal”., Penerbit Dept. PU, Jakarta.
[9] Anonim, 2011, SNI 1974-2011 “Cara Uji Kuat Tekan Beton Dengan Benda Uji Silinder”., Badan Standarisasi Nasional.
[10] Anonim, 2002, SNI 03-6821-2002 “Spesifikasi Agregat Sebagai Bahan Campuran Beton”., Badan Standarisasi Nasional, Jakarta.
[11] Anonim, 2011, SNI 1974:2011 “Cara Uji Kuat Tekan Beton Dengan Benda Uji Silinder”., Badan Standarisasi Nasional, Jakarta.

Downloads

Published

2022-01-29

How to Cite

Juanita, J. (2022). PENINGKATAN NILAI KUAT TEKAN DAN PERBAIKAN RETAK-RETAK PADA BETON DENGAN MENGGUNAKAN FIBER KAWAT BENDRAT BENTUK “Z” DENGAN 3 (TIGA) VARIASI CAMPURAN: Indonesia. J-ENSITEC (Journal Of Engineering and Sustainable Technology), 8(01), 619–623. https://doi.org/10.31949/jensitec.v8i01.1982